Abstract：Silicon-manganese nitride is a new type of raw material for nitriding in steelmaking. At present, the contents of silicon, manganese, phosphorus and iron are usually analyzed by wet chemical method. The experimental procedures are relatively time-consuming and the operation is relatively tedious. The determination method of silicon, manganese, phosphorus and iron in silicon-manganese nitride by X-ray fluorescence (XRF) was established using lithium carbonate as oxidant, lithium tetraborate as flux and ammonium bromide as release agent. The influence of loss on ignition (LOI) was considered during the preparation of calibration curve. The linear range of calibration curve was extended by adding pure materials (such as SiO2 and Fe2O3) into the standard sample of ferromanganese-silicon. Experiments showed that the prepared glass beads had smooth surface without gas pores under the following conditions: the dilution ratio was 1∶20; the mixture was fused in a melting furnace at 1150℃ for 8min. Meanwhile, there were no residues for carbon and nitrogen. The precision results showed that the relative standard deviations (RSD, n=10) of Si, Mn, P and Fe were between 0.36% and 2.3%. Three samples were determined according to the experimental method, and the found results were consistent with those obtained by wet chemical method in national standard method.
刘伟, 张瑜, 杨菊蕾, 王珺. 熔融制样-X射线荧光光谱法测定氮化硅锰中主次组分[J]. 冶金分析, 2020, 40(2): 7-11.
LIU Wei, ZHANG Yu, YANG Ju-lei, WANG Jun. Determination of major and minor components in silicon-manganese nitride by X-ray fluorescence spectrometrywith fusion sample preparation. , 2020, 40(2): 7-11.
宋赞,苏长永,白苗苗,等.氮化硅锰合金的制备技术[J].钢铁研究,2016,44(4):55-58.SONG Zan,SU Chang-yong,BAI Miao-miao,et al.Preparation technology of MnSiN alloy[J].Research on Iron and Steel,2016,44(4):55-58.
[2]
杨勇,吴伟,刘浏.硅锰合金增氮制备氮化硅锰[J].钢铁研究学报,2018,30(6):441-446.YANG Yong,WU Wei,LIU Liu.Preparation of Si-Mn-N alloy by adding nitrogen to silicon-manganese alloy[J].Journal of Iron and Steel Research,2018,2018,30(6):441-446.
[3]
王立新,王烽,曹吉祥,等.冶金仪器分析技术与应用[M].北京:化学工业出版社,2010.
[4]
吉昂,陶光仪,卓尚军,等.X射线荧光光谱分析[M].北京:科学出版社,2003.
[5]
刘伟,曹吉祥,郭云涛,等.熔融制样-X射线荧光光谱法测定硅锰合金中硅锰磷[J].冶金分析,2015,35(8):51-54.LIU Wei,CAO Ji-xiang,GUO Yun-tao,et al.Determination of silicon,manganese,phosphorus in silicon manganese alloy by X-ray fluorescence spectrometry with fusion sample preparation[J].Metallurgical Analysis,2015,35(8):51-54.
[6]
吴超超,陈自斌,邢文青,等.熔融制样-X射线荧光光谱法测定锰铁、硅锰合金中锰硅磷[J].冶金分析,2018,38(3):14-21.WU Chao-chao,CHEN Zi-bin,XING Wen-qing,et al.Determination of manganese,silicon,phosphorus in ferromanganese and silicomanganese alloy by X-ray fluorescence spectrometry with fusion sample preparation[J].Metallurgical Analysis,2018,28(3):14-21.
[7]
李小青.熔融制样-X射线荧光光谱法测定锰铁和金属锰中锰硅磷[J].冶金分析,2018,38(6):39-42.LI Xiao-qing.Determination of manganese,silicon,phosphorus in ferromanganese and manganese metal by X-ray fluorescence spectrometry with fusion sample preparation[J].Metallurgical Analysis,2018,38(6):39-42.
[8]
徐建平.四硼酸锂坩埚内预氧化熔融制样-X-射线荧光光谱法测定锰铁及锰硅合金中的硅、锰、磷[J].理化检验:化学分册(Physical Testing and Chemical Analysis Part B:Chemical Analysis),2016,52(11):1344-1346.
[9]
鲍希波,石毓霞,赵靖,等.熔融制样-X射线荧光光谱法测定硅铁合金中主次元素[J].冶金分析,2010,30(5):14-18.BAO Xi-bo,SHI Yu-xia,ZHAO Jing,et al.X-ray fluorescence spectrometry for the determination of major and minor elements in ferro-silicon alloy with fusion sample preparation[J].Metallurgical Analysis,2010,30(5):14-18.