Abstract： The sample was prepared by fusion using mixed oxidizing agents. The determination method of Al2O3, SiO2, CaO, MgO, Fe2O3, Cr2O3 and TiO2 in alumina carbon refractory materials by X-ray fluorescence spectrometry was established. The effect of mixed oxidizing agent ratio, oxidization time, flux and dilution ratio, release agent and loss on ignition on the sample preparation and analytical results were discussed. The pre-oxidization conditions were determined by orthogonal experiments: the ratio of Na2O2 and sample was 4:1, the ratio of NaNO3 and sample was 2:1, and the pre-oxidization time was 90 min; when lithium tetraborate-lithium metaborate mixed flux (mass ratio of 67:33) was used with dilution ratio of 30:1 and ammonium iodide was used as the release agent, the sample reparation results were best; for the samples with large loss on ignition, they could be determined after ignition, and the ideal results could be obtained based on the loss on ignition and the measured results. It was verified that, the analytical precision of this method was good. The relative standard deviations (RSDs, n=9) of components were 0.29%-2.92%. The analytical results were in good agreement with those obtained by chemical method.
王 珺, 刘 伟, 戴学谦, 任维萍, 张瑞霖. 熔融制样X射线荧光光谱法分析铝碳质耐火材料中的多种组分[J]. 冶金分析, 2013, 33(3): 39-45.
WANG Jun, LIU Wei, DAI Xue-qian, REN Wei-ping, ZHANG Rui-lin. Analysis of various components in alumina carbon refractory materials with X-ray fluorescence spectrometry after sample preparation by fusion. , 2013, 33(3): 39-45.
［3］Hiroyuki Ida, Jun Kawai. Identification of steel by X-ray fluorescence analysis with a pyroelectric X-ray generator［J］. Analytical and Bioanalytical Chemistry, 2004, 379: 735-738.
［4］Aurora G. Coedo, Maria Teresa Dorado, Carlos J. Rivero, et al. X-ray fluorescence analysis of ferroalloys: development of methods for the preparation of test and calibration samples［J］. Analyst, 1994, 119: 421-426.
［7］Hideo Asakura, Katsusige Ikegami, Mamoru Murata, et al. Determination of components in refractories containing zirconia by x-ray fluorescence spectrometry［J］.X-RAY SPECTROMETRY,2000, 29: 418-425.
［8］Lili Vuchkova, Juri Jordanov. Fusion method for preparation of refractory nickel based alloy powders for X-ray fluorescence spectrometry［J］. Analyst, 2000,125: 1681-1685.
［11］宋祖峰,阚斌,陈健. 镁铝铬质耐火材料的X射线荧光光谱分析［J］. 理化检验-化学分册 (Physical Testing and Chemical Analysis Part B:Chemical Analysis), 2005, 41(9): 648-653.
［12］Gazulla M F, Gomez M P, Orduna M, et al. Physico-chemical characterisation of silicon carbide refractories［J］. Journal of the European Ceramic Society, 2006, 26: 3451-3458.