Researches on selection and action mechanism of flux for the determination of trace sulfur in high manganese sainless steel by high frequency combustion-infrared absorption method
REN Wei-ping
Technology Center of Shanxi Taigang Stainless Steel Co., Ltd. , Taiyuan 030003,China
Abstract： Aimed at the phenomenon that the determination results of trace sulfur in high manganese stainless steel by high-frequency combustion infrared absorption method was seriously low, with high manganese stainless steel Cr18Ni5Mn10Mo3 and GH139 as test samples, the influence of type, proportioning, adding order of flux and sample weight was studied. At the same time, the high-temperature oxidation behavior and action mechanism of flux was discussed with the help of thermal analyzer, which provides a theoretical basis for flux selection. The test results showed that the optimal flux dosage and sample adding order for stainless steel Cr18Ni5Mn10Mo3 and GH139 respectively were 0.5 g of pure iron + 0.25 g of sample + 0.5 g of tin + 2.5 g of tungsten, and 0.5 g of tin +0.7 g of pure iron + 0.20 g of sample + 0.5 g of mixture of molybdenum trioxide and vanadium pentoxide (m(MoO3):m(V2O5)) +1.5 g of tungsten, respectively. Sulfur in the two high-manganese stainless steel standard samples was determined by this method, with the measured values in consistency with the certified values and the relative standard deviation of the measurement results in 7.2% and 4.5% (n=6), respectively.
任维萍. 高频燃烧红外吸收法测定高锰不锈钢中痕量硫的助熔剂选择及其作用机理研究[J]. 冶金分析, 2012, 32(11): 26-30.
REN Wei-ping. Researches on selection and action mechanism of flux for the determination of trace sulfur in high manganese sainless steel by high frequency combustion-infrared absorption method. , 2012, 32(11): 26-30.
Chiyoko Miyagi, Kikuko Oomuro, Yosirou Takizawa,et al. Simultaneous determination of ultratrace amounts of carbon and sulfur in steel by an infrared absorption method after combustion in an inductions furnace[J]. Anal.Chem., 2002, 51(11)：1019-1026.
[6]
加藤将彦，平井昭司，Masahiko KATO，et al．管状炉·燃焼赤外線吸収装置を用いた微少量鉄鋼試料中の微量炭素及び硫黄の定量．鉄と鋼(Iron and Steel)，2007，93(2)：112-116.