Cause analysis of drilling cracks in free-cutting silver bright rod
ZHANG Xiaoyu1, SU Mengmeng1, XU Xiangyu1, ZOU Hu2, FU Jianxun*1
1. Center for Advanced Solidification Technology,State Key Laboratory of Advanced Special Steel, School of Materials Science and Engineering,Shanghai University,Shanghai 200444,China; 2. Wuhu Xinxing Ductile Iron Pipes Co., Ltd.,Wuhu 214000,China
Abstract：1215 MS free-cutting steel has good machinability,and its surface quality can directly affect the production and processing of products.After drilling of 1215 MS free-cutting silver bright rod produced by one steel plant,the cracks were observed at the core of the parts.In order to find out the causes of drilling cracks,the corresponding area of the sample was studied by means of scanning electron microscope and energy dispersive spectrometer (SEM/EDS).The results showed that the metallographic structure of 1215 MS free-cutting steel was mainly composed of ferrite + pearlite,which accounted for 92.0% and 4.4%,respectively.The coarse pearlite banded structure was found on the cracking side of the sample,and its equivalent diameter could be up to 15.0 μm,while the equivalent diameter of ordinary pearlite was only 6.2 μm.Compared with the ferrite structure,the average hardness of pearlite structure was higher,which was 243 HV0.01.The high hardness pearlite band led to uneven force of the drill bit during drilling,resulting in material cracking.
张晓宇, 苏蒙蒙, 徐翔宇, 邹虎, 付建勋. 易切削银亮棒钻孔开裂原因解析[J]. 冶金分析, 2024, 44(4): 9-16.
ZHANG Xiaoyu, SU Mengmeng, XU Xiangyu, ZOU Hu, FU Jianxun. Cause analysis of drilling cracks in free-cutting silver bright rod. , 2024, 44(4): 9-16.
[1] 袁武华,王峰.国内外易切削钢的研究现状和前景[J].钢铁研究,2008,36(5):56-62. YUAN Wuhua,WANG Feng.Present research status and prospects on free cutting steel at home and abroad[J].Research on Iron & Steel,2008,36(5):56-62. [2] 曹晨巍,张盼盼,胡绍晖,等.硫系、碲系、铅系易切削钢组织及硫化物对比分析[J].冶金分析,2020,40(7):8-15. CAO Chenwei,ZHANG Panpan,HU Shaohui,et al.Structure and sulfide comparative analysis of sulfur,tellurium and lead free-cutting steels[J].Metallurgical Analysis,2020,40(7):8-15. [3] 黄乔,任英,张立峰.碲处理含硫钢加热过程中MnS-MnTe夹杂物的演变[J].中国冶金,2022,32(7):57-66. HUANG Qiao,REN Ying,ZHANG Lifeng.Evolution of MnS-MnTe inclusions during heating of tellurium treated sulfur-containing steel[J].China Metallurgy,2022,32(7):57-66. [4] Farrugia D C J.High temperature ductile damage during rolling of free cutting steels[J].Ironmaking & Steelmaking,2013,37(4):298-305. [5] Shen P,Zhang D,Zhang H,et al.Study on the three-dimensional morphology of MnS inclusions in high sulphur steel[J].Ironmaking & Steelmaking,2021,48(10):1179-1186. [6] Liu H,Hu D,Fu J.Analysis of MnS inclusions formation in resulphurised steel via modeling and experiments[J]. Materials(Basel),2019,12(12):2028. [7] 胡娟,刘春林,张志明,等.1215MS易切削钢产品质量分析及工艺改进[J].南方金属,2018(3):15-18. HU Juan,LIU Chunlin,ZHANG Zhiming,et al.Quality analysis and process improvement of free cutting steel 1215MS products[J].Southern Metals,2018(3):15-18. [8] 艾克南,张盼盼,赵梦豪,等.1215易切削钢拉拔表面裂纹形成机制分析[J].钢铁,2020,55(2):88-94. AI Kenan,ZHANG Panpan,ZHAO Menghao,et al.Analysis of formation mechanism of surface crack of 1215 free-cutting steel during drawing[J].Iron and Steel,2020,55(2):88-94. [9] Wang J,Wang F,Li C,et al.Simulation of solidification microstructure and columnar to equiaxed transition in free-cutting steel 9SMn28 based on a CAFE method[J].Steel Research International,2010,81(2):150-157. [10] 刘凤连,董凤奎,刘年富.1144易切削钢剪切开裂原因分析[J].热处理技术与装备,2021,42(4):46-49. LIU Fenglian,DONG Fengkui,LIU Nianfu.Cause analysis on shear cracking of 1144 free cutting steel[J].Heat Treatment Technology and Equipment,2021,42(4):46-49. [11] Kim Y,Kim H,Shin S Y,et al.Formation mechanisms of cracks formed during hot rolling of free-machining steel billets[J].Metallurgical and Materials Transactions A,2011,43(3):882-892. [12] 邹虎,王东兴,陈永峰,等.低碳含碲硫易切削钢的研究与实践[J].中国冶金,2020,30(12):77-81,91. ZOU Hu,WANG Dongxing,CHEN Yongfeng,et al.Research and practice of low carbon free-cutting steel containing tellurium and sulfur[J].China Metallurgy,2020,30(12):77-81,91. [13] 周楠,张志明,刘春林,等.1215MS易切削钢铸坯皮下气泡原因分析及改进[J].连铸,2017,42(4):48-52. ZHOU Nan,ZHANG Zhiming,LIU Chunlin,et al.Analysis and control of subcutaneous bubble in 1215MS free cutting steel[J].Continuous Casting,2017,42(4):48-52. [14] 余国松.1215MS易切削钢盘条翘皮成因[J].中国冶金,2014,24(4):26-30. YU Guosong.Causes of 1215MS free cutting steel wire rode warping[J].China Metallurgy,2014,24(4):26-30. [15] 张海波,王敏,高宇波,等.铸坯及轧材中元素偏析行为分析[J].冶金分析,2023,43(9):1-7. ZHANG Haibo,WANG Min,GAO Yubo,et al.Analysis of element segregation behavior in casting billet and rolled product[J].Metallurgical Analysis,2023,43(9):1-7. [16] 邹虎,赵文渊,赵满堂,等.1215MS易切削钢盘条的表面缺陷及其预防措施[J].上海金属,2022,44(2):93-97. ZOU Hu,ZHAO Wenyuan,ZHAO Mantang,et al.Surface defects of 1215MS free cutting steel wire rod and precautions against them[J].Shanghai Metals,2022,44(2):93-97. [17] 黄铸铭,周成宏,廖子东,等.美标SAE1215圆钢表面开裂原因分析[J].热处理技术与装备,2023,44(1):47-50. HUANG Zhuming,ZHOU Chenghong,LIAO Zidong,et al.Analysis of surface cracking causes of American standard SAE1215 round steel[J].Heat Treatment Technology and Equipment,2023,44(1):47-50. [18] 王高峰,李成良,张志明,等.1215MS易切削钢中组织与硫化物分析[J].特殊钢,2020,41(4):64-67. WANG Gaofeng,LI Chengliang,ZHANG Zhiming,et al.Analysis on structure and sulfide in 1215MS free cutting steel[J].Special Steel,2020,41(4):64-67. [19] 张迎晖,赖泓州,赵鸿金.钢中带状组织的研究现状[J].轧钢,2014,31(3):45-47. ZHANG Yinghui,LAI Hongzhou,ZHAO Hongjin.Research status of banded structure in steel[J].Steel Rolling,2014,31(3):45-47. [20] Wang K,Yu T,Song Y,et al.Effects of MnS inclusions on the banded microstructure in non-quenched and tempered steel[J].Metallurgical and Materials Transactions B,2019,50(3):1213-1224. [21] 桂林涛.高硫钢凝固溶质分配系数与MnS析出对偏析的影响研究[D].重庆:重庆大学,2020.