Determination of six components in black corundum by X-ray fluorescence spectrometry with fusion sample preparation
KANG Dehua1,2, YU Yuanjun1,2, LI Ying2, DENG Junhua2, WANG Yiling2
1. State Key Laboratory of Marine Equipment Made of Metal Material and Application, Anshan 114009, China; 2. Iron &Steel Research Institute of Ansteel Group, Anshan 114009, China
摘要 黑刚玉是一种以Al2O3、SiO2和TiO2为主要成分的新型环保材料,其化学成分的分析一般采用滴定法、分光光度法或原子吸收光谱法等,这些方法操作相对繁琐、流程长。实验采用H3BO3-Li2CO3 混合熔剂(m∶m＝7∶3)按质量比为1∶10的稀释比进行熔融制样,加入0.15 g NH4I脱模剂,有效地消除了矿物效应、粒度效应。实验选择矾土、黏土、焦宝石等与黑刚玉组分相似的标准物质和人工合成校准样品建立校准曲线,各组分校准曲线的相关系数均大于0.998,实现了熔融制样-X射线荧光光谱法对黑刚玉中Al2O3、SiO2、Fe2O3、TiO2、CaO和MgO含量的同时测定。对黑刚玉样品进行准确度考察,实验方法的测定值与其他方法的测定值吻合较好,各组分测定结果的相对标准偏差(RSD)均小于2.0%。
Abstract：The black corundum is a kind of new environmental protection material with aluminum oxide, silicon oxide and titanium oxide as the main components. The chemical composition of black corundum is generally analyzed by titration method, spectrophotometry or atomic absorption spectrometry. These methods are relatively cumbersome with long process. In the experiments, H3BO3-Li2CO3 mixed flux (m∶m=7∶3) was used to melt the sample according to the mass ratio of 1∶10. In sample preparation, 0.15 g of NH4I was added as the release agent. The mineral effect and granularity effect were effectively eliminated. The calibration curve was drawn using the artificially synthesized calibration samples and standard materials of bauxite, clay and scorched gemstone, which had similar components to the black corundum. The correlation coefficients of calibration curves were all higher than 0.998. The simultaneous determination of Al2O3, SiO2, Fe2O3, TiO2, Cao and MgO in black corundum by X-ray fluorescence spectrometry (XRF) with fusion sample preparation was realized. The accuracy tests of black corundum sample were conducted. The found results of proposed method were in good agreement with those obtained by other methods. The relative standard deviations (RSD) of determination results were all less than 2.0%.
亢德华, 于媛君, 李颖, 邓军华, 王一凌. 熔融制样-X射线荧光光谱法测定黑刚玉中6种组分[J]. 冶金分析, 2021, 41(2): 40-43.
KANG Dehua, YU Yuanjun, LI Ying, DENG Junhua, WANG Yiling. Determination of six components in black corundum by X-ray fluorescence spectrometry with fusion sample preparation. , 2021, 41(2): 40-43.
崔宏利.熔融制样-X 射线荧光光谱法测定硅质、铝质、镁质和铬质耐火材料中15 种组分[J].冶金分析,2019,39(2):71-76.CUI Hongli.Determination of fifteen components in siliceous,aluminum,magnesia and chrome refractory materials by X-ray fluorescence spectrometry with fusion sample preparation[J].Metallurgical Analysis,2019,39(2):71-76.
[5]
陆晓明,金德龙. X射线荧光光谱法测定含碳化硅铝质耐火材料中9种组分[J].冶金分析,2015,35(7):15-19.LU Xiaoming, JIN Delong.Determinaiton of nine components in aluminum refractory with silicon carbide by X-ray fluorescence spectrometry[J].Metallurgical Analysis,2015,35(7):15-19.
[6]
曲月华. X射线荧光光谱法快速分析高炉渣中TiO2 [J].冶金分析,2003,23(5):40-42.QU Yuehua.Rapid analysis of TiO2 in blast furnace slag by XRF[J].Metallurgical Analysis,2003,23(5):40-42.
曲月华,王翠艳.X射线荧光光谱法测定铝质耐火材料中主次成分[J].冶金分析,2006,26(8):36-40.QU Yuehua,WANG Cuiyan.Determination of major and minor components in alumium refractory by X-ray fluorescence spectrometry[J]. Metallurgical Analysis,2006,26(8):36-40.